Ethanol steam reforming over NiLaZr and NiCuLaZr mixed metal oxide catalysts

CATALISIS

ETANOL

COBRE

NIQUEL

BIOETANOL

BIBLIOGRAFIA NACIONAL QUIMICA

2013

NiLaZr and NiCuLaZr mixed metal oxide catalysts were prepared by co-precipitation with oxalic acid in alcoholic medium, followed by calcination. XRD analysis of the unreduced catalysts showed the formation of crystalline phases corresponding to the pyrochlore structure La2Zr2O7 and NiO following calcination at 850 ◦C, 900 ◦C and 950 ◦C. TEM microscopy of the amorphous solids obtained by calcination at 700 ◦C showed the formation of nanoparticles 20–30 nm in size. TPR analysis showed a shift in the Ni and Cu reduction temperature towards lower values with increasing calcination temperature. All catalysts were active in runs of ethanol steam reforming, leading to the formation of gaseous mixtures containing hydrogen, carbon monoxide, carbon dioxide and methane. Deactivation due to carbon formation was observed at the lowest reaction temperature tested (500 ◦C). XRD, FTIR and thermogravimetric analysis revealed differences in the textural properties of catalysts before and after reforming, which varied in degree according to the catalyst calcination temperature. The NiCuLaZr catalysts showed a lower activity than their NiLaZr analogues, a fact that was ascribed to the formation of a nickel–copper solution, with a lower catalytic activity in the cleavage of C C bonds.

Catalysis Today v. 213, 2013. -- p. 42-49

Elsevier

2013

Información sobre Derechos de Autor

(Por favor lea este aviso antes de abrir los documentos u objetos)

La legislación uruguaya protege el derecho de autor sobre toda creación literaria, científica o artística, tanto en lo que tiene que ver con sus derechos morales, como en lo referente a los derechos patrimoniales con sujeción a lo establecido por el derecho común y las siguientes leyes

(LEY 9.739 DE 17 DE DICIEMBRE DE 1937 SOBRE PROPIEDAD LITERARIA Y ARTISTICA CON LAS MODIFICACIONES INTRODUCIDAS POR LA LEY DE DERECHO DE AUTOR Y DERECHOS CONEXOS No. 17.616 DE 10 DE ENERO DE 2003, LEY 17.805 DE 26 DE AGOSTO DE 2004, LEY 18.046 DE 24 DE OCTUBRE DE 2006 LEY 18.046 DE 24 DE OCTUBRE DE 2006)

ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso: Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con fines de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes debe indicarse el nombre de la persona autora.

PDF

Inglés

Artículo

http://dx.doi.org/10.1016/j.cattod.2013.04.013