Effect of Pt, Pd, Au and Ag on oxidation behaviour of Fe3Al intermetallic

OXIDACION

METALES NOBLES

BIBLIOGRAFIA NACIONAL QUIMICA

2016

A study on the effect of the addition of 1 at-% noble elements such as Pt, Pd, Ag and Au on the oxidation resistance of Fe3Al intermetallic alloy has been carried out at 900, 1000 and 1100°C during 100 h. For comparison, the same tests were performed on a Ni-base alloy type Inconel 600. At all the tested temperatures, parabolic growth rate was observed for the different alloys. The effect of the different noble elements was not unique at the different tested temperature. Thus, at 900°C, addition of Ag increased the mass gain, whereas Pd decreased it; at 1000°C, however, the opposite was true. At 1100°C, the mass gain was decreased by adding Pt, but Pd was very detrimental. In most of the cases, the scales were predominantly formed by Al2O3 with minor amounts of Fe2O3. Scale spallation was found when the noble elements were randomly distributed on the surface, but when they were finely distributed, the scale did not spall. In all cases, the mass gain for Fe3Al alloy was lower than Inconel 600 type alloy.

Corrosion Engineering Science and Technology v. 51, no. 3, 2016.-- p. 179-186

Taylor & Francis

2016

Información sobre Derechos de Autor

(Por favor lea este aviso antes de abrir los documentos u objetos)

La legislación uruguaya protege el derecho de autor sobre toda creación literaria, científica o artística, tanto en lo que tiene que ver con sus derechos morales, como en lo referente a los derechos patrimoniales con sujeción a lo establecido por el derecho común y las siguientes leyes (LEY 9.739 DE 17 DE DICIEMBRE DE 1937 SOBRE PROPIEDAD LITERARIA Y ARTISTICA CON LAS MODIFICACIONES INTRODUCIDAS POR LA LEY DE DERECHO DE AUTOR Y DERECHOS CONEXOS No. 17.616 DE 10 DE ENERO DE 2003, LEY 17.805 DE 26 DE AGOSTO DE 2004, LEY 18.046 DE 24 DE OCTUBRE DE 2006 LEY 18.046 DE 24 DE OCTUBRE DE 2006)

ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso: Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con fines de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes debe indicarse el nombre de la persona autora.

PDF

Inglés

Artículo

DOI: 10.1179/1743278215Y.0000000045

PDF