Enhanced defect-mediated ferromagnetism in Cu2O by Co doping

FERROMAGNETISMO

OXIDO CUPROSO

BIBLIOGRAFIA NACIONAL QUIMICA

2017

In this work an extensive characterization of Co doped Cu2O thin films grown by electrochemical deposition is presented. The doped films showed ferromagnetic behavior, with impressive Curie temperature up to 700 K. Undoped samples also presented magnetic moments at room temperature, but much reduced when compared to doped ones. The observed magnetism in undoped and doped samples was taken as an indicative of a defect-mediated ferromagnetism. Moreover, the sample magnetization was reduced as a consequence of a decreasing in defect density due to thermal annealing. Polarization-dependent X-ray absorption measurements demonstrated that oxygen derived states are the source of the observed magnetic moment and its magnetic dichroism depends on the amount of point defects. Structural, optical and electrical characterization provides information that confirms the incorporation of Co atoms in the Cu2O lattice, without the formation of secondary segregated Co phases. In addition, Electron Paramagnetic Resonance and Glow Discharge Optical Emission Spectroscopy measurements reject the existence of contaminants in the films, dismissing them as the source for the observed magnetism. Computational calculations have shown that Co doping shall locally increases the amount of defects, such as interstitial O, leading to highly oxidized regions from where the unpaired spin arises. This situation generates a picture similar to the magnetic polaron theory, but with the dopant ion pinning the defects.

Journal of Magnetism and Magnetic Materials v. 441, 2017. -- p. 374-386

Elsevier

2017

Información sobre Derechos de Autor

(Por favor lea este aviso antes de abrir los documentos u objetos)

La legislación uruguaya protege el derecho de autor sobre toda creación literaria, científica o artística, tanto en lo que tiene que ver con sus derechos morales, como en lo referente a los derechos patrimoniales con sujeción a lo establecido por el derecho común y las siguientes leyes (LEY 9.739 DE 17 DE DICIEMBRE DE 1937 SOBRE PROPIEDAD LITERARIA Y ARTISTICA CON LAS MODIFICACIONES INTRODUCIDAS POR LA LEY DE DERECHO DE AUTOR Y DERECHOS CONEXOS No. 17.616 DE 10 DE ENERO DE 2003, LEY 17.805 DE 26 DE AGOSTO DE 2004, LEY 18.046 DE 24 DE OCTUBRE DE 2006 LEY 18.046 DE 24 DE OCTUBRE DE 2006)

ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso: Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con fines de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes debe indicarse el nombre de la persona autora.

PDF

Inglés

Artículo

DOI: 10.1016/j.jmmm.2017.05.057

PDF