Phase, nucleation and coalescence of Hgl2 onto amorphous substrates

Dublin Core

Título

Phase, nucleation and coalescence of Hgl2 onto amorphous substrates

Tema

CRISTALOGRAFIA
2008
BIBLIOGRAFÍA NACIONAL QUÍMICA

Abstract

Heterogeneous nucleation and further growth of HgI2 onto glass were studied by the physical vapor deposition (PVD) method, with and without an argon atmosphere. Glass substrates 2″×2″ in area were used for nucleation and growth. Supersaturation strongly determined not only the nuclei population and size, but also the HgI2 nucleation phase. A range of nucleation–growth temperatures between 303 and 333 K for the substrate, and a range of initial argon pressure between 1.3 and 2.6×104 Pa were found appropriate for nucleation and growth in the α (red) phase of HgI2. Other conditions, such as an argon pressure higher than 4×104 Pa, determined the nucleation and growth in the β (yellow) metastable phase. After a nucleation growth time of 30 min, clusters of about 0.5 μm for β-HgI2 and 1 μm for α-HgI2 and a minimum distance between the clusters of about 1 and 10 μm were, respectively, obtained. Coalescence was performed by annealing the clusters at a temperature between 303 and 333 K and from 5 min to 24 h, at an initial argon pressure of 104 Pa. They coalesced to form larger clusters, which, in the case of the β-phase also transformed to the α-stable phase. From the experimental nucleation–growth and further coalescence conditions, correlations between supersaturation conditions and phase were established. Also, considerations about interface free energies and nucleation phase were made. Future work will be conducted to diminish nuclei size and enlarge nuclei population, seeking for early stages of nucleation.

Autor

Noguera, Ana Lía
Perez, María Eugenia
Quagliata, Eduardo

Fuente

Journal of Crystal Growth v. 310, no.7-9, 2008. -- p.1691-1696

Editor

Elsevier

Fecha

2008

Derechos

Información sobre Derechos de Autor

(Por favor lea este aviso antes de abrir los documentos u objetos)

La legislación uruguaya protege el derecho de autor sobre toda creación literaria, científica o artística, tanto en lo que tiene que ver con sus derechos morales, como en lo referente a los derechos patrimoniales con sujeción a lo establecido por el derecho común y las siguientes leyes

(LEY 9.739 DE 17 DE DICIEMBRE DE 1937 SOBRE PROPIEDAD LITERARIA Y ARTISTICA CON LAS MODIFICACIONES INTRODUCIDAS POR LA LEY DE DERECHO DE AUTOR Y DERECHOS CONEXOS No. 17.616 DE 10 DE ENERO DE 2003, LEY 17.805 DE 26 DE AGOSTO DE 2004, LEY 18.046 DE 24 DE OCTUBRE DE 2006 LEY 18.046 DE 24 DE OCTUBRE DE 2006)

ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso: Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con fines de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes debe indicarse el nombre de la persona autora.

Formato

PDF

Idioma

Inglés

Tipo

Artículo

Identificador

DOI: 10.1016/j.jcrysgro.2007.12.005
Fecha de agregación
October 24, 2014
Colección
Bibliografía Nacional Química
Tipo de Elemento
Document
Etiquetas
Citación
Noguera, Ana Lía, “Phase, nucleation and coalescence of Hgl2 onto amorphous substrates,” RIQUIM - Repositorio Institucional de la Facultad de Química - UdelaR, accessed November 21, 2019, http://riquim.fq.edu.uy/items/show/1989.
Archivos