High catalytic activity at low temperature in oxidative dehydrogenation of propane with Cr–Al pillared clay

ARCILLAS

CATALISIS

PROPANO

BIBLIOGRAFIA NACIONAL QUIMICA

2014

A montmorillonite was pillared separately with chromium and aluminum polyoxocations (Cr–C and Al–C respectively) and also with an equimolar mixture of both polioxocations (Al–Cr–C). The resulting solids were characterized by scanning electron microscopy, energy dispersive spectrometry, thermal analysis, Fourier transform infrared spectroscopy, X-ray diffraction and nitrogen adsorption at 196 C. The inclusion of polycations in the interlamellar space led to modifications in the properties of the clay. An eleven fold increase in specific surface area with respect to the calcined starting clay was found for the Al–C, whereas a twofold increase was observed for the Cr–C; the value for the Al–Cr–C was only slightly higher than that for the latter. Diffractograms of the Cr–C showed the occurrence of a Cr2O3 phase. Catalytic activity in oxidative dehydrogenation of propane was assayed in the temperature range from 350 C to 450 C using Ar/C3H8/O2 (80/10/10) as reactant gas mixture. Propylene selectivity was found to be temperature- dependent, showing a maximum in the studied temperature range for the catalyst containing only aluminum, whereas remaining practically constant for the Cr-containing catalysts. Highly promising propylene yields at low temperature were obtained with the catalyst containing Al and Cr (Al–Cr–C): 9.3% at 350 C and 10.3% at 450 C.

Chemical Engineering Journal  v. 241, 2014. -- p. 336-343

Elsevier

2014

Información sobre Derechos de Autor

(Por favor lea este aviso antes de abrir los documentos u objetos)

La legislación uruguaya protege el derecho de autor sobre toda creación literaria, científica o artística, tanto en lo que tiene que ver con sus derechos morales, como en lo referente a los derechos patrimoniales con sujeción a lo establecido por el derecho común y las siguientes leyes

(LEY 9.739 DE 17 DE DICIEMBRE DE 1937 SOBRE PROPIEDAD LITERARIA Y ARTISTICA CON LAS MODIFICACIONES INTRODUCIDAS POR LA LEY DE DERECHO DE AUTOR Y DERECHOS CONEXOS No. 17.616 DE 10 DE ENERO DE 2003, LEY 17.805 DE 26 DE AGOSTO DE 2004, LEY 18.046 DE 24 DE OCTUBRE DE 2006 LEY 18.046 DE 24 DE OCTUBRE DE 2006)

ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso: Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con fines de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes debe indicarse el nombre de la persona autora.

PDF

Inglés

Artículo

http://dx.doi.org/10.1016/j.cej.2013.10.086

PDF