Biocarbon monoliths as supercapacitor electrodes : Influence of wood anisotropy on their electrical and electrochemical properties

Dublin Core

Título

Biocarbon monoliths as supercapacitor electrodes : Influence of wood anisotropy on their electrical and electrochemical properties

Tema

MADERA
ELECTROQUIMICA
MONOLITOS DE BIOCARBON
BIBLIOGRAFIA NACIONAL QUIMICA
2014

Abstract

Biocarbon monoliths were obtained from Eucalyptus grandis and the influence of wood anisotropy on the electrical and electrochemical performance as supercapacitor electrodes was studied. They were produced from wood pieces cut along the transversal and longitudinal direction of the tree trunk, followed by pyrolysis and, for some of them, also by activation with CO2. Monoliths with drilled channels were also obtained. All the monoliths were characterized by SEM, nitrogen adsorption/desorption isotherms, electrical conductivity measurements and electrochemical measurements, the latter in 2M aqueous H2SO4 electrolyte. Electrical conductivity and specific capacitance are higher for the transversal carbon monoliths than for the longitudinal ones. The electrical conductivity reaches values up to 27 S cm−1 for the transversal monolith. The specific capacitance reaches values up to 260 F g−1 for the transversal monolith that was activated and drilled. However, the highest volumetric capacitance, of 90 F cm−3, is found for the longitudinal monolith that was activated and non-drilled. The energy density and power density, both referred to gravimetric and volumetric magnitudes, reach values as high as 36 Wh kg−1 and 12 Wh L−1, and 2181 W kg−1 and 783 W L−1, respectively. Comparison with a commercial powder activated carbon is provided

Autor

Cuña, Andrés
Barranco, Violeta
Centeno, Teresa A.
Quevedo, Angie
Rojo, José M.

Fuente

Journal of the Electrochemical Society v. 161, no. 12, 2014. -- p. A1806-A18011

Editor

The Electrochemical Society

Fecha

2014

Derechos

Información sobre Derechos de Autor

(Por favor lea este aviso antes de abrir los documentos u objetos)

La legislación uruguaya protege el derecho de autor sobre toda creación literaria, científica o artística, tanto en lo que tiene que ver con sus derechos morales, como en lo referente a los derechos patrimoniales con sujeción a lo establecido por el derecho común y las siguientes leyes

(LEY 9.739 DE 17 DE DICIEMBRE DE 1937 SOBRE PROPIEDAD LITERARIA Y ARTISTICA CON LAS MODIFICACIONES INTRODUCIDAS POR LA LEY DE DERECHO DE AUTOR Y DERECHOS CONEXOS No. 17.616 DE 10 DE ENERO DE 2003, LEY 17.805 DE 26 DE AGOSTO DE 2004, LEY 18.046 DE 24 DE OCTUBRE DE 2006 LEY 18.046 DE 24 DE OCTUBRE DE 2006)

ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso: Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con fines de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes debe indicarse el nombre de la persona autora.



Formato

PDF

Idioma

Inglés

Tipo

Artículo

Identificador

DOI: 10.1149/2.0391412jes

Document Item Type Metadata

Original Format

PDF
Fecha de agregación
April 13, 2015
Colección
Bibliografía Nacional Química
Tipo de Elemento
Document
Etiquetas
, ,
Citación
Cuña, Andrés, “Biocarbon monoliths as supercapacitor electrodes : Influence of wood anisotropy on their electrical and electrochemical properties,” RIQUIM - Repositorio Institucional de la Facultad de Química - UdelaR, accessed October 14, 2019, http://riquim.fq.edu.uy/items/show/2731.
Archivos