Rubidium−Alkaline-Earth Trifluoroacetate Hybrids as Self- Fluorinating Single-Source Precursors to Mixed-Metal Fluorides

Dublin Core

Título

Rubidium−Alkaline-Earth Trifluoroacetate Hybrids as Self- Fluorinating Single-Source Precursors to Mixed-Metal Fluorides

Tema

METALES
RUBIDIO
CRISTALES HIBRIDOS BIMETALICOS
BIBLIOGRAFIA NACIONAL QUIMICA
2019

Abstract

Three novel bimetallic hybrid crystals featuring rubidium–alkaline-earth metal pairs and trifluoroacetato ligands were synthesized, and their utility as self-fluorinating single-source precursors to the corresponding mixed-metal fluorides was demonstrated. Rb2Mg2(tfa)6(tfaH)2·3H2O, RbCa(tfa)3, and RbSr2(tfa)5 (tfa = CF3COO–; tfaH = CF3COOH) were synthesized in both single-crystal and polycrystalline forms via solvent evaporation. Their crystal structures were solved using single-crystal X-ray diffraction (XRD), and chemical purity was confirmed using thermal analysis (TGA/DTA). Metal–oxygen–metal connectivity in Rb2Mg2(tfa)6(tfaH)2·3H2O was restricted to four-metal building blocks. In contrast, RbCa(tfa)3 and RbSr2(tfa)5 were found to be extended inorganic hybrids (Cheetham et al. Chem. Commun. 2006, 0, 4780−4795) exhibiting infinite metal connectivity in three and two dimensions, respectively. Systematic analysis of the coordination modes of the trifluoroacetato ligand revealed its ability to bridge alkali and alkaline-earth metals. Rietveld analysis of powder X-ray diffraction data (PXRD) showed that thermal decomposition of Rb2Mg2(tfa)6(tfaH)2·3H2O and RbCa(tfa)3 under inert atmosphere yielded crystalline RbMgF3 and RbCaF3, respectively. This solid-state transformation occurred without the need for an external fluorinating agent because the trifluoromethyl group acted as a built-in fluorine source. Solid-state and solution thermolysis of Rb2Mg2(tfa)6(tfaH)2·3H2O provided access to the hexagonal and cubic polymorphs of the fluoroperovskite RbMgF3, respectively. Findings reported in this article highlight that bimetallic trifluoroacetates offer unique features from the standpoint of both crystal lattice topology and reactivity.

Autor

Szlag, Regina G.
Dhanapala, B. Dulani
Rabuffetti, Federico A.

Fuente

Inorganic Chemistry  v. 58, 2019. -- p. 3041-3049

Editor

American Chemical Society

Fecha

2019

Derechos

Información sobre Derechos de Autor

(Por favor lea este aviso antes de abrir los documentos u objetos)

La legislación uruguaya protege el derecho de autor sobre toda creación literaria, científica o artística, tanto en lo que tiene que ver con sus derechos morales, como en lo referente a los derechos patrimoniales con sujeción a lo establecido por el derecho común y las siguientes leyes (LEY 9.739 DE 17 DE DICIEMBRE DE 1937 SOBRE PROPIEDAD LITERARIA Y ARTISTICA CON LAS MODIFICACIONES INTRODUCIDAS POR LA LEY DE DERECHO DE AUTOR Y DERECHOS CONEXOS No. 17.616 DE 10 DE ENERO DE 2003, LEY 17.805 DE 26 DE AGOSTO DE 2004, LEY 18.046 DE 24 DE OCTUBRE DE 2006)

ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso: Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con fines de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes debe indicarse el nombre de la persona autora.

Formato

PDF

Idioma

Inglés

Tipo

Artículo

Identificador

DOI: 10.1021/acs.inorgchem.8b02988

Document Item Type Metadata

Original Format

PDF
Fecha de agregación
July 30, 2019
Colección
Bibliografía Nacional Química
Tipo de Elemento
Document
Etiquetas
, ,
Citación
Szlag, Regina G., “Rubidium−Alkaline-Earth Trifluoroacetate Hybrids as Self- Fluorinating Single-Source Precursors to Mixed-Metal Fluorides,” RIQUIM - Repositorio Institucional de la Facultad de Química - UdelaR, accessed August 21, 2019, http://riquim.fq.edu.uy/items/show/5818.
Archivos